Item
|
Test method
|
Unit
|
PF370
|
|
Base polymer
|
ASTM
|
|
PA-6
|
|
Components
(filler, etc.)
|
Organic
|
|
Physical
|
Specific gravity (ρ)
|
D792
|
-
|
3.70
|
|
Water absorption
(23ºC/24Hrs/
in water)
|
D570
|
wt%
|
0.2 |
|
Molding
shrinkage (MD/td)
|
D955
|
%
|
0.4/0.5
|
|
Mechanical
|
Tensile strength
|
D638
|
MPa
|
70
|
|
Elongation
|
D638
|
%
|
0.3
|
|
Flexural strength
|
D790
|
MPa
|
108
|
|
Flex. Modulus
of elasticity
|
D790
|
GPa
|
21
|
|
Izod impact
strength notched
|
D256
|
J/m
|
39
|
|
Rockwell hardness
R scale
|
D785
|
-
|
118
|
|
Thermal
|
Heat deflection
temperature
under load
(18.2MPa)
|
D648
|
ºC
|
178
|
|
Flammability
(UL-94 V Class)
|
-
|
HB
|
|
Electrical
|
Volume resistivity
|
SB Method
|
Ω•cm
|
106
|
|
Molding
conditions
|
Prior drying
(temperature ºC×hours)
|
ºC×Hrs
|
10 0×3
|
|
Cylinder temperature
|
ºC
|
270-320
|
|
Mold temperature
|
ºC
|
80-120
|