Unclad laminates SUMILITE^® PL/EL

	Unclad laminates Top

	Unclad laminates for electronic parts

	Unclad laminates for electric & electronic apparatus and appliances via punching

	Unclad laminates for machines and electrical apparatus via machining

	Unclad laminates for carriers

	Unclad laminates for reinforcing FPC (Flexible Printed Circuits)

	Super-Hemit (Insulation board)

Unclad laminates for machines and electrical apparatus via machining

Features and characteristics EL-3762

Formulation		Corresponding standards JIS (ANSI)		Article No.	Thickness
Resin	Base material
Epoxy resin	Glass cloth	GEF	FR-4	EL-3762	13

Properties		Unit	Processing Conditioning
Flatwise dielectric strength		MV/m	C-90/20/65	18
Edgewise dielectric strength		KV	O-0.5/90	45
Insulation resistance		MΩ	C-90/20/65	2×10⁹
			D-2/100	3×10⁸
Heat resistivity		-	A	150ºC, 120min.
Flexural strength	MD	Mpa	A	390
	TD			370
Tensile strength	MD	Mpa	A	340
	TD			310
Compression strength	vertical	Mpa	A	350
	parallel			200
Izod impact strength (parallel to layer)	MD	J/cm	A	7.1
	TD			6.6
Bonding strength		KN	A	10.8
Water absorption		%	E-24/50+D-24/23	0.01
Solvent resistivity		(Acetone resistivity)	Boiling for 30 min.	Constant
Specific gravity		-	-	1.8
Dimensional ranges	Size	mm	-	1000×1000
	Thickness			3.0-50.0
Note		-	-	94-V-0

Note1: Tests were performed according to JIS K6911.

Note2: The alphabet indicates the kind of conditioning of test piece.
A: as received without conditioning; C: conditioned in air at constant temperature and humidity; D: immersed in water at constant temperature; E: conditioned in air at constant temperature; O: immersed in oil at constant temperature
The data mentioned above is not guarantee value but representative one.